PC LEXAN™ 124R-111 SABIC INNOVATIVE US

123

Unit Price:
$3091 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
38.1MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:transparent High mobility
Application Areas:Non specific food
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	24 hr	ASTM D570	0.15	%
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35	%
	Water absorption rate	Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58	%
Melt flow rate	300°C/1.2 kg	ASTM D1238	18	g/10 min
Specific volume		ASTM D792	0.830	cm³/g
Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending modulus	50.0 mm Span	ASTM D790	2340	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	96.0	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile strength 2	Yield	ASTM D638	62.0	Mpa
Tensile strength 2	Tensile strength 2	Break	ASTM D638	68.0	Mpa
Elongation rate 2	Yield	ASTM D638	7.0	%
Elongation rate 2	Elongation rate 2	Break	ASTM D638	130	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature		ASTM D15255	154	°C
specific heat		ASTM C351	1250	J/kg/°C
thermal conductivity		ASTM C177	0.19	W/m/K
RTI		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
Linear coefficient of thermal expansion - flow	-40 to 95°C	ASTM E831	6.8E-5	cm/cm/°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	129	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 2
Hot wire ignition (HWI)		UL 746	PLC 2
Dielectric constant	60 Hz	ASTM D150	3.17
	Dielectric constant	50 kHz	ASTM D150	3.17
	Dielectric constant	Dielectric constant	1 MHz	ASTM D150	2.96
Volume resistivity		ASTM D257	> 1.0E+17	ohms·cm
Dissipation factor	50 Hz	ASTM D150	9.0E-4
	Dissipation factor	60 Hz	ASTM D150	9.0E-4
	Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.010
Dielectric strength	3.20 mm, in Air	ASTM D149	15	KV/mm
High arc combustion index (HAI) 6		UL 746	PLC 1
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 2

injection	Test Result	Unit
drying temperature	120	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	280 到 305	°C
Mold temperature	70 到 95	°C
drying time	3.0 到 4.0	hr
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	260 到 280	°C
Temperature in the middle of the barrel	270 到 295	°C
Temperature at the front of the material cylinder	280 到 305	°C
Spray nozzle temperature	275 到 300	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Tensile impact strength 4		ASTM D1822	546	kJ/m²
Falling hammer impact	23°C	ASTM D3029	169	J
Non notched cantilever beam impact	23°C	ASTM D4812	3200	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTM D785	70
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ASTM D542	1.586
Haze	2540 µm	ASTM D1003	1.0	%
transmissivity	2540 µm	ASTM D1003	88.0	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.