PC LEXAN™ 3412ECR-131/739 SABIC INNOVATIVE US
115
- Unit Price:
- $2678 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 107.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced enhance Flame retardant High rigidity
- Application Areas:Electrical appliances Electronic display Industrial applications Automotive External Parts Medical supplies Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.50 | % |
| TD：3.20mm | 内部方法 | 0.20to0.50 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.29 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 7.0 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 7.00 | cm3/10min |
| Density/specific gravity | ASTMD792 | 1.30 | g/cm³ | |
| ISO1183 | 1.36 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 5 | ISO178 | 5500 | Mpa | |
| Bending strength 5,6 | ISO178 | 140 | Mpa | |
| Elongation rate 3 | Yield | ASTMD638 | 3.1 | % |
| Tensile modulus 2 | ASTMD638 | 5500 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 87.0 | Mpa |
| Yield | ASTMD638 | 90.0 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 5000 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 156 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 95.0 | Mpa |
| Break | ISO527-2/5 | 90.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 2.8 | % |
| Break | ISO527-2/5 | 3.2 | % | |
| Tensile modulus | ISO527-2/1 | 6000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 141 | °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 3E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 3E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 130 | °C | |
| RTIStr | UL746 | 130 | °C | |
| Vicat softening temperature | ASTMD152510 | 147 | °C | |
| -- | ISO306/B50 | 145 | °C | |
| -- | ISO306/B120 | 146 | °C | |
| Hot deformation temperature 9 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 141 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 136 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance 11 | ASTMD495 | PLC7 | ||
| Hot wire ignition | HWI | UL746 | PLC0 | |
| High arc combustion index | HAI | UL746 | PLC3 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Relative permittivity | 50Hz | IEC60250 | 3.30 | |
| 60Hz | IEC60250 | 3.30 | ||
| 1MHz | IEC60250 | 3.30 | ||
| Dissipation factor | 50Hz | IEC60250 | 0.020 | |
| 60Hz | IEC60250 | 0.020 | ||
| 1MHz | IEC60250 | 0.010 | ||
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 20.0 | J |
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | 35 | kJ/m² |
| 23°C | ISO180/1U | 35 | kJ/m² | |
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 5.0 | kJ/m² |
| 23°C | ISO179/1eA | 6.0 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 40 | kJ/m² | |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 6.0 | kJ/m² |
| 23°C | ISO180/1A | 7.0 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 110 | J/m |
| 23°C | ASTMD256 | 110 | J/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ISO4589-2 | 40 | % | |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.