PC CALIBRE™ 201-22 STYRON US
117
- Unit Price:
- $3210 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:Food containers
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD792 | 1.20 | g/cm³ | |
| ISO1183/A | 1.20 | g/cm³ | ||
| ISO11832 | 1200 | kg/m3 | ||
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 22 | g/10min |
| 300°C/1.2kg | ISO1133 | 22 | g/10min | |
| Meltvolume-flowrate | 300°C/1.2kg | ISO11332 | 18.0 | cm3/10min |
| Shrinkage rate | MD | ASTMD955 | 0.50to0.70 | % |
| MD | ISO294-4 | 0.50to0.70 | % | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.15 | % |
| 23°C,24hr | ISO62 | 0.15 | % | |
| Equilibrium,23°C,50%RH | ASTMD570 | 0.32 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.32 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 3 | ASTMD638 | 2340 | Mpa | |
| Tensile modulus | ISO527-2/50 | 2300 | Mpa | |
| ISO527-22 | 2300 | Mpa | ||
| Tensile strength 3 | Yield | ASTMD638 | 60.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 60.0 | Mpa |
| Yield | ISO527-22 | 60.0 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 65.5 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 66.0 | Mpa |
| Tensile strain | Yield | ISO527-22 | 6.0 | % |
| Elongation rate 4 | Break | ASTMD638 | 120 | % |
| Tensile strain | Break | ISO527-2/50 | 120 | % |
| Nominal strainatbreak | ISO527-22 | >50 | % | |
| Bending modulus 4 | ASTMD790 | 2410 | Mpa | |
| Bending modulus 5 | ISO178 | 2400 | Mpa | |
| Bending strength 4 | ASTMD790 | 96.5 | Mpa | |
| Bending stress 5 | ISO178 | 97.0 | Mpa | |
| Taber abraser | ASTMD1044 | 45 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 139 | °C |
| 0.45MPa,Annealed | ASTMD648 | 142 | °C | |
| 0.45MPa,Annealed | ISO75-2/B | 142 | °C | |
| 0.45MPa | ISO75-22 | 142 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 126 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 139 | °C | |
| 1.8MPa,Annealed | ISO75-2/A | 126 | °C | |
| 1.8MPa | ISO75-22 | 128 | °C | |
| Vicat softening temperature | ASTMD15257 | 147 | °C | |
| ISO306/B50 | 147 | °C | ||
| 50N | ISO3062 | 147 | °C | |
| Ball pressure temperature | IEC60335-1 | 125 | °C | |
| Linear coefficient of thermal expansion | MD：-40to82°C | ASTMD696 | 6.8E-05 | cm/cm/°C |
| MD | ISO11359-22 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTMD257 | 2E+17 | ohms·cm | |
| IEC600932 | >1.0E+13 | ohms·m | ||
| Dielectric strength | ASTMD149 | 17 | KV/mm | |
| IEC60243-1 | 17 | KV/mm | ||
| Electrical strength | IEC60243-12 | 17 | KV/mm | |
| Dielectric constant | 60Hz | ASTMD150 | 3.00 | |
| 1MHz | ASTMD150 | 3.00 | ||
| Relative permittivity | 100Hz | IEC602502 | 3.00 | |
| 1MHz | IEC602502 | 3.00 | ||
| Dissipation factor | 50Hz | ASTMD150 | 1E-03 | |
| 1MHz | ASTMD150 | 2E-03 | ||
| 100Hz | IEC602502 | 1E-03 | ||
| 1MHz | IEC602502 | 2E-03 | ||
| Compared to the anti leakage trace index | 2.00mm,SolutionA | IEC60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile impact strength | ASTMD1822 | 378 | kJ/m² | |
| Charpynotchedimimpact string | 23°C | ISO179/1eA2 | 70.0 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA2 | 11.0 | kJ/m² |
| Charpy impact strength | 23°C | ISO179/1eU2 | NoBreak | |
| Charpyimpactstrength | -30°C | ISO179/1eU2 | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 750 | J/m |
| 23°C | ISO180/A | 74 | kJ/m² | |
| 23°C | ASTMD256 | NoBreak | ||
| Unscented Izod impact strength | 23°C | ISO180 | NoBreak | |
| InstrumentedDartImpact6 | 23°C,TotalEnergy | ASTMD3763 | 72.3 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ASTMD785 | 72 | |
| R-Sale | ASTMD785 | 118 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTMD542 | 1.586 | ||
| ISO489 | 1.586 | |||
| transmissivity | ASTMD1003 | 89.0 | % | |
| Haze | ASTMD1003 | 1.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating 8 | 1.6mm | UL94 | HB | |
| 3.2mm | UL94 | HB | ||
| BurningBehav.at1.6mmnom.thickn. | 1.60mm,UL | ISO12102 | HB | |
| Burning Behav.atthicknessh | 3.20mm,UL | ISO12102 | HB | |
| Extreme Oxygen Index 8 | ISO4589-2 | 26 | % | |
| Oxygenindex | ISO4589-22 | 26 | % | |
| Average degree of combustion | ASTMD635 | 3 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.