PC PANLITE® G-3430H TEIJIN JAPAN
201
- Unit Price:
- $5604 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low anisotropy enhance Flame retardant
- Application Areas:Engineering accessories Mechanical components Camera applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molding shrinkage rate | ASTM D955 | 0.30-0.50 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.12 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.30到0.50 | % |
| MD:4.00mm | 内部方法 | 0.10到0.30 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 6700 | Mpa | |
| Tensile stress | Break | ISO527-2/5 | 100 | Mpa |
| Tensile strain | Break | ISO527-2/5 | 2.0 | % |
| Bending modulus 3 | ISO178 | 6600 | Mpa | |
| Bending stress 3 | ISO178 | 155 | Mpa | |
| elongation at break | ASTM D638/ISO 527 | 3.0 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 6700 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 108 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 93 | ||
| Bending modulus | ASTM D790/ISO 178 | 6600 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 155 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 146 | ℃（℉） | |
| vicat softening point | ASTM D1525/ISO R306 | 146 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000060 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 143 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 139 | °C | |
| Vicat softening temperature | ISO306/B50 | 146 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 3E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6E-05 | cm/cm/°C | |
| RTIElec | 1.5mm | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 125 | °C |
| RTI | 1.5mm | UL746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength 4 | IEC60243-1 | 35 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.50 | |
| 1MHz | IEC60250 | 3.50 | ||
| Dissipation factor | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 9E-03 | ||
| Leakage Trace Index | IEC60112 | 175 | V | |
| Dielectric loss | ASTM D150/IEC 60250 | 0.0010 | ||
| ASTM D150/IEC 60250 | 0.0090 | |||
| Surface resistivity | ASTM D257/IEC 60093 | 1.0E+15 | Ω | |
| Dielectric constant | ASTM D150/IEC 60250 | 3.50 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 1.0E+15 | Ω.cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 45 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.43mm | UL94 | HB | |
| 0.8mm | UL94 | V-2 | ||
| 3.0mm | UL94 | V-1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.