PC PANLITE® G-3110PH TEIJIN JAPAN
209
- Unit Price:
- $3013 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced
- Application Areas:Electrical applications Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1270 | ||
| Molding shrinkage rate | ASTM D955 | 0.35-0.55 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.16 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.40to0.60 | % |
| MD:4.00mm | 内部方法 | 0.35to0.55 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.16 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 3000 | Mpa | |
| Tensile stress | Break | ISO527-2/5 | 65.0 | Mpa |
| elongation at break | ASTM D638/ISO 527 | 5.0 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 3000 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 3100 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 110 | kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | Break | ISO527-2/5 | 5.0 | % |
| Bending modulus 2 | ISO178 | 3100 | Mpa | |
| Bending stress 2 | ISO178 | 110 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 123 | ℃（℉） | |
| vicat softening point | ASTM D1525/ISO R306 | 134 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.5 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 130 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 123 | °C | |
| Vicat softening temperature | ISO306/B50 | 134 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 5E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6E-05 | cm/cm/°C | |
| RTIElec | 1.7mm | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | 1.7mm | UL746 | 120 | °C |
| RTIStr | 1.7mm | UL746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength 3 | IEC60243-1 | 35 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.20 | |
| 1MHz | IEC60250 | 3.20 | ||
| Dissipation factor | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 9E-03 | ||
| Leakage Trace Index | IEC60112 | 175 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 55 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | HB | |
| 1.7mm | UL94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.