PC PANLITE® LV-2225Z TEIJIN SINGAPORE

108

Unit Price:
$3920 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low viscosity transparent UV resistance
Application Areas:Electrical field Electronic field currency
Color:--
Grade:High liquidity level

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.2

physical property	Test Condition	Test Method	Test Result	Unit
Melt volume flow rate	300°C/1.2kg	ISO1133	15.0	cm3/10min
Shrinkage rate	TD:4.00mm	内部方法	0.50to0.70	%
Shrinkage rate	Shrinkage rate	MD:4.00mm	内部方法	0.50to0.70	%
Water absorption rate	23°C,24hr	ISO62	0.20	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2/1	2400	Mpa
Tensile stress	Yield	ISO527-2/50	61.0	Mpa
Tensile strain	Yield	ISO527-2/50	6.0	%
elongation at break		ASTM D638/ISO 527	50	%
Tensile modulus		ASTM D638/ISO 527	2130	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M 77
Bending modulus		ASTM D790/ISO 178	2260	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	94	kg/cm²(MPa)[Lb/in²]
Nominal tensile fracture strain		ISO527-2/50	>50	%
Bending modulus 2		ISO178	2400	Mpa
Bending stress 2		ISO178	94.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility (rate)		UL94	V-2
vicat softening point		ASTM D1525/ISO R306	148	℃（℉）
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	141	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	125	°C
Vicat softening temperature		ISO306/B50	146	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	7E-05	cm/cm/°C
RTIElec	1.5mm	UL746	125	°C
Evolution Calendar intelligent importer	1.5mm	UL746	115	°C
RTIStr	1.5mm	UL746	125	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	>1.0E+15	ohms
Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Dielectric strength 3		IEC60243-1	30	KV/mm
Dielectric constant	100Hz	IEC60250	3.10
Dielectric constant	Dielectric constant	1MHz	IEC60250	3.00
Dissipation factor	100Hz	IEC60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC60250	9E-03
Leakage Trace Index		IEC60112	225	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	NoBreak

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ASTMD542	1.585
transmissivity	3000µm	ASTMD1003	88.0	%
Light transmittance		ASTM D1003/ISO 13468	88	%
Refractive index		ASTM D542/ISO 489	1.585

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40mm	UL94	V-2
	UL flame retardant rating	1.5mm	UL94	V-2
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-2
Burning wire flammability index	1.5mm	IEC60695-2-12	850	°C
Burning wire flammability index	Burning wire flammability index	3.0mm	IEC60695-2-12	960	°C
Hot filament ignition temperature	1.5mm	IEC60695-2-13	850	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC60695-2-13	875	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.