PC PANLITE® L-1225Z100 TEIJIN JAPAN

115

Unit Price:
$2087 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance transparent
Application Areas:Translucent accessories lens Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Method	Test Result	Unit
density	ASTM D792/ISO 1183	/1200
Molding shrinkage rate	ASTM D955	0.5-0.7	%
Water absorption rate 23 ℃/24h	ASTM D570/ISO 62	0.2	%

physical property	Test Condition	Test Method	Test Result	Unit
Melt volume flow rate	300°C/1.2kg	ISO1133	12.0	cm3/10min
Shrinkage rate	TD:4.00mm	内部方法	0.50to0.70	%
Shrinkage rate	Shrinkage rate	MD:4.00mm	内部方法	0.50to0.70	%
Water absorption rate	23°C,24hr	ISO62	0.20	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2/1	2400	Mpa
Tensile stress	Yield	ISO527-2/50	61.0	Mpa
Tensile strain	Yield	ISO527-2/50	6.0	%
Nominal tensile fracture strain		ISO527-2/50	>50	%
Bending modulus 2		ISO178	2400	Mpa
Bending stress 2		ISO178	94.0	Mpa
Tensile modulus		ASTM D638/ISO 527	/2400	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	/61	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	/6	%
Bending modulus		ASTM D790/ISO 178	/2400	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	/94	kg/cm²(MPa)[Lb/in²]

Thermal performance	Test Condition	Test Method	Test Result	Unit
vicat softening point		ASTM D1525/ISO R306	148	℃（℉）
Linear expansion coefficient		ASTM D696/ISO 11359	0.7	mm/mm.℃
RTIStr	1.5mm	UL746	125	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	141	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	128	°C
Vicat softening temperature		ISO306/B50	148	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	7E-05	cm/cm/°C
RTIElec	1.5mm	UL746	125	°C
Evolution Calendar intelligent importer	1.5mm	UL746	115	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	>1.0E+15	ohms
Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Dielectric strength 3		IEC60243-1	30	KV/mm
Relative permittivity	100Hz	IEC60250	3.10
Relative permittivity	Relative permittivity	1MHz	IEC60250	3.00
Dissipation factor	100Hz	IEC60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC60250	9E-03
Leakage Trace Index		IEC60112	250	V
Dielectric constant		ASTM D150/IEC 60250	3.1
Dielectric constant	Dielectric constant		ASTM D150/IEC 60250	3

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch		ISO179	NoBreak

optical performance	Test Condition	Test Method	Test Result	Unit
Light transmittance		ASTM D1003/ISO 13468	88	%
Refractive index		ASTM D542/ISO 489	1.585
Refractive index	Refractive index		ASTMD542	1.585
transmissivity	3000µm	ASTMD1003	88.0	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.9mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	0.40mm	UL94	V-2
Burning wire flammability index	1.5mm	IEC60695-2-12	825	°C
Burning wire flammability index	Burning wire flammability index	3.2mm	IEC60695-2-12	875	°C
Hot filament ignition temperature	1.5mm	IEC60695-2-13	850	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.2mm	IEC60695-2-13	875	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.