PC PANLITE® K-1300Y TEIJIN JAPAN
202
- Unit Price:
- $3583 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 81MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent
- Application Areas:Translucent accessories film sheet Cleaning Compound transparent
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1200 | ||
| Molding shrinkage rate | ASTM D955 | 0.5~0.7 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.2 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23℃,24hrs | ISO 62 | 0.2 | % |
| Shrinkage rate | 0.5-0.7 | % | ||
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 2.80 | cm3/10min |
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.50to0.70 | % |
| MD:4.00mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.20 | % |
| Melting volume flow rate | ISO 1133 | 2.5 | CM |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-1 | 2350 | Mpa | |
| Tensile yield stress | ISO 527-1 | 60 | Mpa | |
| Tensile yield elongation | ISO 527-1 | 6 | % | |
| elongation | Break | ISO 527-1 | ＞50 | % |
| Bending modulus | ISO 178 | 2200 | Mpa | |
| Izod notched impact strength | 没Notched | ISO 179 | NB | KJ/m |
| 带Notched | ISO 179 | 89 | KJ/m | |
| Tensile modulus | ISO527-2/1 | 2350 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 60.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Nominal tensile fracture strain | ISO527-2/50 | >50 | % | |
| Bending modulus 2 | ISO178 | 2200 | Mpa | |
| Bending stress 2 | ISO178 | 90.0 | Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 6 | % | |
| Bending modulus | ASTM D790/ISO 178 | 2200 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 90 | kg/cm²(MPa)[Lb/in²] | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 89 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | >50 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.80MPa | ISO 75-1 | 132 | °C |
| vicat softening point | ISO 306 | 151 | °C | |
| Coefficient of linear expansion | ISO 11359-2 | 0.7 | ||
| Flame retardancy | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 145 | ℃（℉） | |
| vicat softening point | ASTM D1525/ISO R306 | 151 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 145 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 132 | °C | |
| Vicat softening temperature | ISO306/B50 | 151 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7E-05 | cm/cm/°C | |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength 3 | IEC60243-1 | 30 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.10 | |
| Dielectric constant | -，100HZ | IEC 60250 | 3.1 | |
| -，1MHz | IEC 60250 | 3 | ||
| dielectric loss tangent | -，100HZ | IEC 60250 | 10 | |
| -，1MHZ | IEC 60250 | 90 | ||
| Volume resistivity | IEC 60093 | ＞1×10 | Ω.m | |
| Surface resistivity | IEC 60093 | ＞1×10 | Ω | |
| ASTM D257/IEC 60093 | >1×10 15 | Ω | ||
| Dielectric constant | ASTM D150/IEC 60250 | 3 | ||
| ASTM D150/IEC 60250 | 3.1 | |||
| Arc resistance | ASTM D495/IEC 60112 | 30 | ||
| Volume resistivity | ASTM D257/IEC 60093 | >1×10 13 | Ω.cm | |
| Relative permittivity | 1MHz | IEC60250 | 3.00 | |
| Dissipation factor | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 9E-03 | ||
| Leakage Trace Index | IEC60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | NoBreak |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTMD542 | 1.585 | ||
| transmissivity | 3000µm | ASTMD1003 | 88.0 | % |
| Light transmittance | 3mm厚 | ASTM D1003 | 88 | % |
| ASTM D1003/ISO 13468 | 88 | % | ||
| Refractive index | ASTM D542/ISO 489 | 1.585 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.38mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.