Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Molding shrinkage rate | | ASTM D955 | 0.5~0.7 | % |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.2 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 18.0 | cm3/10min |
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.50to0.70 | % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2/1 | 2400 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 61.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Nominal tensile fracture strain | | ISO527-2/50 | >50 | % |
| Bending modulus 2 | | ISO178 | 2350 | Mpa |
| Bending stress 2 | | ISO178 | 93.0 | Mpa |
| Tensile modulus | | ASTM D638/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 6 | % |
| Bending modulus | | ASTM D790/ISO 178 | 2350 | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 93 | kg/cm²(MPa)[Lb/in²] |
| Tensile elongation at break (elongation at break) | | ASTM D638/ISO 527 | >50 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| vicat softening point | | ASTM D1525/ISO R306 | 146 | ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 139 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 126 | °C |
| Vicat softening temperature | | ISO306/B50 | 146 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 7E-05 | cm/cm/°C |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Dielectric strength 3 | | IEC60243-1 | 30 | KV/mm |
| Relative permittivity | 100Hz | IEC60250 | 3.10 | |
| Relative permittivity | 1MHz | IEC60250 | 3.00 | |
| Dissipation factor | 100Hz | IEC60250 | 1E-03 | |
| Dissipation factor | 1MHz | IEC60250 | 9E-03 | |
| Leakage Trace Index | | IEC60112 | 250 | V |
| Surface resistivity | | ASTM D257/IEC 60093 | >1×1015 | Ω |
| Dielectric constant | | ASTM D150/IEC 60250 | 3 | |
| Dielectric constant | | ASTM D150/IEC 60250 | 3.1 | |
| Arc resistance | | ASTM D495/IEC 60112 | 30 | |
| Volume resistivity | | ASTM D257/IEC 60093 | >1×1013 | Ω.cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | NoBreak | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ASTMD542 | 1.585 | |
| transmissivity | 3000µm | ASTMD1003 | 88.0 | % |
| Light transmittance | | ASTM D1003/ISO 13468 | 88 | % |
| Refractive index | | ASTM D542/ISO 489 | 1.585 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 875 | °C |
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 850 | °C |
| UL flame retardant rating | 1.9mm | UL94 | HB | |
| UL flame retardant rating | 0.40mm | UL94 | V-2 | |
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.