PC TARFLON™ G-2530 IDEMITSU JAPAN
204
- Unit Price:
- $3426 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 78.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent Flame retardant enhance
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.42 | ||
| Molding shrinkage rate | ASTM D955 | 1.5 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.11 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Spiral flow length | 3mm厚 | 出光法 | 23 | CM |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile elasticity | ISO R-527 (ASTM D-638) | 8100(83000) | MPa(KG/cm | |
| Flexural elasticity | ISO 178 (ASTM D-790) | 8530(8700) | MPa(KG/cm | |
| Tensile failure rate | ISO R-527 (ASTM D-638) | 3 | % | |
| tensile strength | ASTM D638/ISO 527 | 8100(83000) | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | M92 | ||
| Bending modulus | ASTM D790/ISO 178 | 8530(8700) | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 170(1700) | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ISO 2039-2 (ASTM D-785) | M92 | ||
| Tensile strength | ISO R-527 (ASTM D-638) | 120(1200) | MPa(KG/cm | |
| Flexural strength | ISO 178 (ASTM D-790) | 170(1700) | Mpa | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 15(16) | kg·cm/cm(J/M)ft·lb/in | |
| IZOD impact strength | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 15(16) | KJ/m |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 3 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | V-2 | ||
| vicat softening point | ASTM D1525/ISO R306 | 150 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 2.3 | mm/mm.℃ | |
| vicat softening point | ISO 306 | 150 | °C | |
| Coefficient of linear expansion | ASTM D-696 | 2.3 | ||
| Combustibility | 1.47mm厚 | UL 94 | V-2 | |
| Load deflection temperature | 1.80MPa,18.6kg/cm | ISO 75(ASTM D-648) | 144 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Induced positive connection | 60Hz | ASTM D-150 | 8×10 | |
| 10 | ASTM D-150 | 9×10 | ||
| Inherent resistance of volume | ASTM D-257 | ＜10 | Ω·cm | |
| permittivity | 10 | ASTM D-150 | 3.45 | |
| Insulation breakdown voltage | 1.6mm厚 | ASTM D-149 | ＜22 | KV/mm |
| permittivity | 60Hz | ASTM D-150 | 3.40 | |
| Arc resistance | ASTM D-495 | 110 | sec |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ASTM D-955 | 1.5 | |
| TD | ASTM D-955 | 6.0 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23℃水中24h | ASTM D-570 | 0.11 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.