PC IUPILON™ GS2010MLR MITSUBISHI ENGINEERING JAPAN

111

Unit Price:
$2567 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20.2MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:enhance Filler: Glass fiber reinf 10% filler by weight
Application Areas:Camera applications
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.27
Molding shrinkage rate		ASTM D955	0.3 - 0.5	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:3.20mm		0.40to0.60	%
Shrinkage rate	Shrinkage rate	MD:3.20mm		0.30to0.50	%
Water absorption rate	Saturation,23°C	ISO62	0.14	%
Melt mass flow rate	300°C/1.2kg	ISO1133	10	g/10min
Melt volume flow rate	300°C/1.2kg	ISO1133	9.00	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress		ISO178	135	Mpa
Tensile stress	Break	ISO527-2	78.0	Mpa
Tensile strain	Break	ISO527-2	2.9	%
elongation at break		ASTM D638/ISO 527	4.6	%
Tensile modulus		ASTM D638/ISO 527	3300	kg/cm²(MPa)[Lb/in²]
Tensile modulus	Tensile modulus		ISO527-2	4500	Mpa
Bending modulus		ASTM D790/ISO 178	2800	kg/cm²(MPa)[Lb/in²]
Bending modulus	Bending modulus		ISO178	4000	Mpa
bending strength		ASTM D790/ISO 178	105	kg/cm²(MPa)[Lb/in²]

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	145	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	140	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	4E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	6.7E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Compared to the anti leakage trace index	CTI	UL746	PLC4

Processing performance	Test Condition	Test Result	Unit
Mold temperature		80-120	°C
Processing temperature		270-290	°C
Processing temperature	Processing temperature		280-300	°C
Dry conditions		热风干燥 120℃---約4-8小时
Screw speed		50-100	rpm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	55	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
FlameRating	0.75mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.