Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1200 | |
| Molding shrinkage rate | | ASTM D955 | 0.5-0.7 | % |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.2 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.50to0.70 | % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.20 | % |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 8.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | Yield | ISO527-2/50 | 61.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Bending modulus 2 | | ISO178 | 2300 | Mpa |
| Bending stress 2 | | ISO178 | 91.0 | Mpa |
| Nominal tensile fracture strain | | ISO527-2/50 | >50 | % |
| Tensile modulus | | ASTM D638/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] |
| Tensile modulus | | ISO527-2/1 | 2400 | Mpa |
| tensile strength | | ASTM D638/ISO 527 | 61 | kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 6 | % |
| Bending modulus | | ASTM D790/ISO 178 | 2300 | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 91 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 142 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 129 | °C |
| vicat softening point | | ASTM D1525/ISO R306 | 149 | ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ |
| Vicat softening temperature | | ISO306/B50 | 149 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 7E-05 | cm/cm/°C |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 100Hz | IEC60250 | 1E-03 | |
| Dissipation factor | 1MHz | IEC60250 | 9E-03 | |
| Relative permittivity | 100Hz | IEC60250 | 3.10 | |
| Relative permittivity | 1MHz | IEC60250 | 3.00 | |
| Leakage Trace Index | | IEC60112 | 250 | V |
| Surface resistivity | | IEC60093 | >1.0E+15 | ohms |
| Dielectric constant | | ASTM D150/IEC 60250 | 3.1 | |
| Dielectric constant | | ASTM D150/IEC 60250 | 3 | |
| Volume resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Dielectric strength 3 | | IEC60243-1 | 30 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | NoBreak | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| transmissivity | 3000µm | ASTMD1003 | 88.0 | % |
| Light transmittance | | ASTM D1003/ISO 13468 | 88 | % |
| Refractive index | | ASTM D542/ISO 489 | 1.585 | |
| Refractive index | | ASTMD542 | 1.585 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.40mm | UL94 | V-2 | |
| UL flame retardant rating | 1.5mm | UL94 | V-2 | |
| UL flame retardant rating | 3.0mm | UL94 | V-2 | |
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 875 | °C |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 850 | °C |
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 875 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.