PC Makrolon® 3208 COVESTRO THAILAND
119
- Unit Price:
- $6222 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance high molecular weight Drinking water contact
- Application Areas:building materials Transportation equipment Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % | |
| TD:2.00mm3 | ISO294-4 | 0.75 | % | |
| MD:2.00mm3 | ISO294-4 | 0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 5.5 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 5.00 | cm3/10min |
| Density/specific gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
| Apparent density 2 | ISO60 | 0.66 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strain 5 | 23°C | ISO178 | 7.2 | % |
| TensileCreepModule | 1hr | ISO899-1 | 2200 | Mpa |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Bending stress 4 | 23°C | ISO178 | 95.0 | Mpa |
| 3.5%Strain,23°C | ISO178 | 72.0 | Mpa | |
| Bending modulus 4 | 23°C | ISO178 | 2350 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2/50 | 65.0 | Mpa |
| Break,23°C | ISO527-2/50 | 75.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2/50 | 6.3 | % |
| Break,23°C | ISO527-2/50 | 120 | % | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1900 | Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 2350 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 142 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 130 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 150 | °C |
| -- | ISO306/B120 | 151 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| BallPressure Test | 141°C | IEC60695-10-2 | Pass | |
| Glass transition temperature 8 | ISO11357-2 | 150 | °C | |
| Thermal conductivity coefficient 9 | 23°C | ISO8302 | 0.20 | W/m/K |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 65.0 | J |
| -30°C | ISO6603-2 | 75.0 | J | |
| Impact strength of simply supported beam gap 6 | -30°C,Complete Break | ISO7391 | 18 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 80 | kJ/m² | |
| Suspended wall beam gap impact strength 7 | -30°C,Complete Break | ISO7391 | 20 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 75 | kJ/m² | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6700 | N |
| 23°C | ISO6603-2 | 5800 | N | |
| Impact strength of simply supported beam without notch | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 111 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index 10 | ISO489 | 1.587 | ||
| Haze | 3000µm | ISO14782 | <0.80 | % |
| transmissivity | 1000µm | ISO13468-2 | 89.0 | % |
| 2000µm | ISO13468-2 | 89.0 | % | |
| 3000µm | ISO13468-2 | 88.0 | % | |
| 4000µm | ISO13468-2 | 87.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlashIgnitionTemperature | ASTMD1929 | 480 | °C | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO7391-PC,M,(,,)-05-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.