POM Delrin® II100 NC010 DUPONT USA
120
- Unit Price:
- $4234 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 65.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity High hardness Thermal stability high viscosity heat-resisting
- Application Areas:Thin walled products Electrical tools
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.8 | % |
| MD | ISO294-4 | 2.2 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.90 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MediumDensity | 1.19 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 3000 | J/kg/°C | ||
| Melt mass flow rate | ISO1133 | 2.3 | g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 1.90 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 2900 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 45 | % | |
| Bending stress | 3.5%Strain | ISO178 | 79.0 | Mpa |
| Compressive stress | ISO604 | 110 | Mpa | |
| Tensile stress | Yield | ISO527-2 | 72.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 26 | % |
| Tensile creep modulus | 1000hr | ISO899-1 | 1600 | Mpa |
| Tensile modulus | ISO527-2 | 3000 | Mpa | |
| Bending modulus | ISO178 | 2900 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 160 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 100 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 175 | °C |
| -- | ISO306/B50 | 160 | °C | |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：AnnealingTemperature | ISO11359-2 | 160 | °C | |
| TD：AnnealingTime-Optional | ISO11359-2 | 30.0 | min/mm | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 1E-07 | m²/s | |
| MD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Melting temperature 2 | ISO11357-3 | 178 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 3E+13 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 41 | KV/mm | |
| Dissipation factor | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 5.5E-03 | ||
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.80 | ||
| Leakage Trace Index | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 430 | kJ/m² |
| 23°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 90 | |
| R-Sale | ISO2039-2 | 121 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| atomization | F-value(refraction) | ISO6452 | 91 | % |
| G-value(condensate) | ISO6452 | 1E-04 | g | |
| Burning rate 3 | 1.00mm | ISO3795 | 30 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg | |
| EmissionofOrganicCompounds | VDA277 | 4.00 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.