POM Delrin® 500AL BK642 DUPONT USA
104
- Unit Price:
- $7271 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Fatigue resistance High impact resistance
- Application Areas:Electrical field Electronic field Industrial applications Household appliances Fitness equipment Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.30 | % |
| Shrinkage rate | TD | ISO294-4 | 1.7 | % |
| MD | ISO294-4 | 1.8 | % | |
| Melt mass flow rate | ISO1133 | 14 | g/10min | |
| MediumDensity | 1.18 | g/cm³ | ||
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 12.0 | cm3/10min |
| Density/specific gravity | ISO1183 | 1.39 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 2400 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 23 | % | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1600 | Mpa |
| Tensile stress | Yield | ISO527-2 | 66.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 11 | % |
| Tensile modulus | ISO527-2 | 3000 | Mpa | |
| Bending modulus | ISO178 | 2800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 164 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 97.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| Melting temperature 2 | ISO11357-3 | 178 | °C | |
| AnnealingTemperature | 160 | °C | ||
| AnnealingTime-Optional | 30.0 | min/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 6.0 | kJ/m² |
| 23°C | ISO179/1eA | 7.0 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 6.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 130 | kJ/m² |
| 23°C | ISO179/1eU | 160 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate 3 | 1.00mm | ISO3795 | 28 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.