POM Delrin® 570 BK DUPONT USA
109
- Unit Price:
- $2706 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 110MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant High temperature resistan Filler: Glass fiber reinf 20% filler by weight 20% filler by weight UV resistance
- Application Areas:Electrical tools household electrical appl
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.2 | % |
| MD | ISO294-4 | 1.8 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.80 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.10 | % | |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 7.00 | cm3/10min |
| Density/specific gravity | ISO1183 | 1.56 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO527-2 | 53.0 | Mpa |
| Tensile strain | Break | ISO527-2 | 12 | % |
| Tensile modulus | ISO527-2 | 4900 | Mpa | |
| Bending modulus | ISO178 | 4600 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 165 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 6E-05 | cm/cm/°C |
| TD | ISO11359-2 | 8.5E-05 | cm/cm/°C | |
| Melting temperature 2 | ISO11357-3 | 178 | °C | |
| AnnealingTemperature | 160 | °C | ||
| AnnealingTime-Optional | 30.0 | min/mm | ||
| Vicat softening temperature | ISO306/B50 | 160 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.90 | ||
| Leakage Trace Index | IEC60112 | 600 | V | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 50 | kJ/m² |
| 23°C | ISO179/1eU | 54 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.0 | kJ/m² |
| 23°C | ISO179/1eA | 3.5 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 6.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 5E-04 | g |
| Burning rate 3 | 1.00mm | ISO3795 | 53 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg | |
| EmissionofOrganicCompounds | VDA277 | 4.80 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.