POM LNP™ LUBRICOMP™ KL-4010 GY SABIC INNOVATIVE US
106
- Unit Price:
- $3537 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant
- Application Areas:Electronic and Electrical
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：24hr | ASTMD955 | 2.3 | % |
| TD：24hr | ASTMD955 | 2.3 | % | |
| TD:24hr | ISO294-4 | 2.3 | % | |
| MD:24hr | ISO294-4 | 2.3 | % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 2760 | Mpa | |
| Bending modulus | ISO178 | 2000 | Mpa | |
| bending strength | ASTMD790 | 13.8 | Mpa | |
| Bending stress | ISO178 | 70.0 | Mpa | |
| friction coefficient | Dynamic | ASTMD3702Modified | 0.38 | |
| Static | ASTMD3702Modified | 0.18 | ||
| Wear factor - Washer | ASTMD3702Modified | 22.5 | 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ISO527-2/1 | 2620 | Mpa | |
| Tensile strength | Yield | ASTMD638 | 55.2 | Mpa |
| Tensile stress | Yield | ISO527-2 | 54.0 | Mpa |
| Tensile strength | Break | ASTMD638 | 52.4 | Mpa |
| Tensile stress | Break | ISO527-2 | 53.0 | Mpa |
| elongation | Yield | ASTMD638 | 9.9 | % |
| Tensile strain | Yield | ISO527-2 | 11 | % |
| elongation | Break | ASTMD638 | 34 | % |
| Tensile strain | Break | ISO527-2 | 30 | % |
| Bending modulus | ASTMD790 | 3450 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 158 | °C |
| Hot deformation temperature 4 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 149 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 112 | °C |
| Hot deformation temperature 4 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 96.0 | °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 1.2E-04 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 5.30 | J |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 0.900 | J | |
| Suspended wall beam gap impact strength 3 | 23°C | ISO180/1A | 48 | kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 1000 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.