Material Description

Technical Data Sheet

Material Description

Material Properties:High rigidity High hardness Thermal stability high viscosity heat-resisting
Application Areas:Thin walled products Electrical tools
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	ISO 294-4	1.5	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	1.8	%
Melt flow rate	190°C/2.16 kg	ISO 1133	2.0	g/10 min
Molten Volume Flow Rate (MVR)	190°C/2.16 kg	ISO 1133	1.70	cm3/10min
density		ISO 1183	1.41	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Poisson's ratio		ISO 527	0.37
Tensile stress	Break	ISO 527-2	65.0	Mpa
Tensile strain	Break	ISO 527-2	15	%
Tensile modulus		ISO 527-2	3100	Mpa
Bending modulus		ISO 178	3000	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	160	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	98.0	°C
Annealing Time - Optional			30.0	min/mm
annealing temperature			160	°C
Melting temperature 2		ISO 11357-3	178	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.1E-4	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 23°C	ISO 11359-2	9.4E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.0E-4	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 23°C	ISO 11359-2	9.2E-5	cm/cm/°C

Filling analysis	Test Condition	Test Method	Test Result	Unit
Melt density			1.18	g/cm³

injection	Test Condition	Test Method	Test Result	Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 到 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			210 到 220	°C
Melt Temperature, Optimum			215	°C
Mold temperature			80 到 100	°C
Mold Temperature, Optimum			90	°C
Maintain pressure			90.0 到 110	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			8.00	s/mm

squeeze	Test Result	Unit
drying temperature	75 到 85	°C
drying time	2.0 到 4.0	hr
Suggested maximum moisture content	0.20	%
Melt Temperature	195 到 205	°C
Extrusion Melt Temperature, Optimum	200	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.5	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate	1.00 mm	ISO 3795	34	mm/min
FMVSS flammability		FMVSS 302	B

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.