POM HOSTAFORM® M25AE CELANESE USA
115
- Unit Price:
- $2512 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 90.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high viscosity wear resistant High sliding enhance
- Application Areas:Electrical tools Cable Electric wire Household appliances Household appliances Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ASTMD955 | 2.2 | % |
| TD | ASTMD955 | 1.8 | % | |
| Melt mass flow rate | ASTMD1238 | 2.5 | g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 2.20 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.8 | % |
| MD | ISO294-4 | 2.2 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.75 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.20 | % | |
| Density of Melt | 内部方法 | 1.200 | g/cm³ | |
| SpecificHeatCapacity of Melt | 内部方法 | 2210 | J/kg/°C | |
| ThermalConductivityofMelt | 内部方法 | 0.16 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield,71°C | ASTMD638 | 34.5 | Mpa |
| Tensile stress | Yield | ISO527-2/1A/50 | 63.0 | Mpa |
| Tensile strain | Yield | ISO527-2/1A/50 | 12 | % |
| TensileCreepModule | 1hr | ISO899-1 | 2100 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1100 | Mpa |
| Bending modulus | 23°C | ISO178 | 2430 | Mpa |
| Tensile modulus | ISO527-2/1A/1 | 2460 | Mpa | |
| Tensile strength | Yield,-40°C | ASTMD638 | 94.5 | Mpa |
| Yield,23°C | ASTMD638 | 60.7 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature 2 | ISO11357-3 | 166 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 110 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 94.0 | °C | |
| Peak melting temperature | ASTMD3418 | 165 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTMD257 | 1E+14 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 190 | kJ/m² |
| 23°C,Partial Break | ISO179/1eU | 250 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.