POM Delrin® 500 WT401 DUPONT USA

107

Unit Price:
$2568 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
90MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High rigidity heat-resisting High impact resistance Thermal stability
Application Areas:Gear Electrical tools Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	1.8	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.9	%
Water absorption rate	Saturation,23°C,2.00mm	ISO62	1.0	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.25	%
Melt mass flow rate		ISO1133	15	g/10min
Melt volume flow rate	190°C/2.16kg	ISO1133	12.0	cm3/10min
Density/specific gravity		ISO1183	1.41	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Nominal tensile fracture strain		ISO527-2	25	%
Tensile modulus		ISO527-2	3100	Mpa
Bending modulus		ISO178	2900	Mpa
Tensile stress	Yield	ISO527-2	67.0	Mpa
Tensile strain	Yield	ISO527-2	15	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	158	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	90.0	°C
Melting temperature 2		ISO11357-3	178	°C
Vicat softening temperature		ISO306/B50	160	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	1.1E-04	cm/cm/°C
AnnealingTemperature			160	°C
AnnealingTime-Optional			30.0	min/mm

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	100Hz	IEC60250	4.20
Relative permittivity	Relative permittivity	1MHz	IEC60250	4.10
Leakage Trace Index		IEC60112	600	V
Surface resistivity		IEC60093	>1.0E+15	ohms

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	290	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	350	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	8.0	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO180/1A	9.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	9.0	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale	ISO2039-2	92
Rockwell hardness	Rockwell hardness	R-Sale	ISO2039-2	120

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.75mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
Burning rate 3	1.00mm	ISO3795	28	mm/min

Supplementary Information	Test Condition	Test Method	Test Result	Unit
Emission		VDA275	<8.00	mg/kg
EmissionofOrganicCompounds		VDA277	6.00	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.