POM Delrin® 100 NC010 DUPONT JAPAN
204
- Unit Price:
- $3300 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 113MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity High hardness Thermal stability high viscosity heat-resisting
- Application Areas:Thin walled products Electrical tools
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | ISO1133 | 2.3 | g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 1.90 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.8 | % |
| MD | ISO294-4 | 2.2 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.90 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MediumDensity | 1.19 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 3000 | J/kg/°C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 3000 | Mpa | |
| Tensile stress | Yield | ISO527-2 | 72.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 26 | % |
| Nominal tensile fracture strain | ISO527-2 | 45 | % | |
| TensileCreepModule | 1hr | ISO899-1 | 2900 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1600 | Mpa |
| Bending modulus | ISO178 | 2900 | Mpa | |
| Bending stress | 3.5%Strain | ISO178 | 79.0 | Mpa |
| Compressive stress | ISO604 | 110 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：AnnealingTemperature | ISO11359-2 | 160 | °C | |
| TD：AnnealingTime-Optional | ISO11359-2 | 30.0 | min/mm | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 1E-07 | m²/s | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 160 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 100 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 175 | °C |
| -- | ISO306/B50 | 160 | °C | |
| Melting temperature 2 | ISO11357-3 | 178 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 3E+13 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 41 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.80 | ||
| Dissipation factor | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 5.5E-03 | ||
| Leakage Trace Index | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 430 | kJ/m² |
| 23°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 90 | |
| R-Sale | ISO2039-2 | 121 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate 3 | 1.00mm | ISO3795 | 30 | mm/min |
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| atomization | F-value(refraction) | ISO6452 | 91 | % |
| G-value(condensate) | ISO6452 | 1E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg | |
| EmissionofOrganicCompounds | VDA277 | 4.00 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.