POM DURACON® GH-20(2) BK JAPAN POLYPLASTIC
121
- Unit Price:
- $3119 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity High hardness Low contractility Low warpage Anti creep VOC 20% filler by weight 20% filler by weight Filler: Glass fiber reinf
- Application Areas:Gear Industrial machinery machine Mechanical components Automotive sector bearing
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:2.00mm | ISO294-4 | 1.0 | % |
| MD:2.00mm | ISO294-4 | 0.80 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.70 | % |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 3.0 | g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 2.30 | cm3/10min |
| Density/specific gravity | ISO1183 | 1.54 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | ISO178 | 135 | Mpa | |
| friction coefficient | Dynamic2 | JISK7218 | 0.42 | |
| Steel - Dynamic3 | JISK7218 | 0.55 | ||
| Wear factor | 0.49MPa,0.30m/sec4 | JISK7218 | 200 | 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec5 | JISK7218 | 300 | 10^-8mm³/N·m | |
| 0.49MPa,0.30m/sec6 | JISK7218 | 7000 | 10^-8mm³/N·m | |
| 0.060MPa,0.15m/sec7 | JISK7218 | 10000 | 10^-8mm³/N·m | |
| Tensile modulus | ISO527-2 | 7000 | Mpa | |
| Bending modulus | ISO178 | 6000 | Mpa | |
| Tensile stress | ISO527-2 | 100 | Mpa | |
| Tensile strain | Break | ISO527-2 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23to55°C | 内部方法 | 3E-05 | cm/cm/°C |
| TD：23to55°C | 内部方法 | 1E-04 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 158 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.2 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 85 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ColourNumber | CF3500 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.