Material Description

Technical Data Sheet

Material Description

Material Properties:Photostability Low wear Weather resistance
Application Areas:Automotive sector Automotive interior parts
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	1.9	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	2.0	%
Water absorption rate	23°C,24hr	ISO62	0.50	%
	Water absorption rate	Saturation,23°C,2.00mm	ISO62	1.2	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.20	%
Melt mass flow rate	190°C/2.16kg	ISO1133	15	g/10min
Melt volume flow rate	190°C/2.16kg	ISO1133	13.0	cm3/10min
Density/specific gravity		ISO1183	1.42	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress		ISO178	77.0	Mpa
Nominal tensile fracture strain		ISO527-2	30	%
Poisson's ratio		ISO527	0.37
Tensile stress	Yield	ISO527-2	70.0	Mpa
Tensile strain	Yield	ISO527-2	17	%
Tensile modulus		ISO527-2	3100	Mpa
Bending modulus		ISO178	3000	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	163	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	95.0	°C
Vicat softening temperature	--	ISO306/A50	174	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B50	160	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	1.2E-04	cm/cm/°C
Melting temperature 2		ISO11357-3	178	°C
AnnealingTemperature			160	°C
AnnealingTime-Optional			30.0	min/mm

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	100Hz	IEC60250	3.80
Relative permittivity	Relative permittivity	1MHz	IEC60250	3.80
Leakage Trace Index		IEC60112	600	V
Dissipation factor	100Hz	IEC60250	2.1E-03
Dissipation factor	Dissipation factor	1MHz	IEC60250	5.6E-03
Surface resistivity		IEC60093	2E+13	ohms
Volume resistivity		IEC60093	>1.0E+15	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	260	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	260	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	8.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	9.0	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO180/1A	8.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	8.0	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale	ISO2039-2	92
Rockwell hardness	Rockwell hardness	R-Sale	ISO2039-2	120

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	0.8mm	IEC60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
atomization	F-value(refraction)4	ISO6452	90	%
atomization	atomization	G-value(condensate)	ISO6452	2E-04	g
Burning rate 3	1.00mm	ISO3795	21	mm/min

Supplementary Information	Test Method	Test Result	Unit
EmissionofOrganicCompounds	VDA277	16.0	µgC/g
Odor	VDA270	6.00
Emission	VDA275	<8.00	mg/kg

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.