POM LNP™ LUBRICOMP™ KFL-4016 SABIC INNOVATIVE US
99
- Unit Price:
- $4513 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan UV resistance
- Application Areas:household electrical appl Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | Internal Method | 0.90 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO 527-2/5 | 49.0 | Mpa |
| Tensile strain | Yield | ISO 527-2/5 | 1.9 | % |
| Tensile modulus | ISO 527-2/1 | 5900 | Mpa | |
| Bending modulus | ISO 178 | 5400 | Mpa | |
| bending strength | ISO 178 | 80.0 | Mpa | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.0 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO 180/1U | 15 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed, 64.0 mm Span | ISO 75-2/Af | 138 | °C |
| Linear expansion coefficient | Flow : 23 to 60°C | ISO 11359-2 | 0.000046 | cm/cm/°C |
| Across Flow : 23 to 60°C | ISO 11359-2 | 0.00010 | cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.