Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 2.1 | % |
| Shrinkage rate | MD | ISO294-4 | 2.1 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.80 | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
| Apparent density | | | 0.85 | g/cm³ |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 11.0 | cm3/10min |
| Density/specific gravity | | ISO1183 | 1.41 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal tensile fracture strain | | ISO527-2/50 | 30 | % |
| Tensile creep modulus 2 | 1000hr | ISO899-1 | 1450 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 66.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 9.0 | % |
| Tensile modulus | | ISO527-2 | 3000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 100 | °C |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 171 | °C |
| Maximum operating temperature - sortcycle operation | | | 100 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 1MHz | IEC60250 | 5E-03 | |
| Dielectric strength | | IEC60243-1 | 85 | KV/mm |
| Relative permittivity | 1MHz | IEC60250 | 3.70 | |
| Leakage Trace Index | SolutionA | IEC60112 | 600 | V |
| Surface resistivity | | IEC60093 | 1E+15 | ohms |
| Volume resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 170 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 170 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 5.5 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.5 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 155 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability level | 1.6mm | IEC60695-11-10,-20 | HB | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ISOType | | ISO9988-1 | POM-K,M-GNR,04-002 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.