Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ISO1183 | 1.32 | g/cm³ |
| Water absorption rate | 23°C,24hr | ISO62 | 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Wear factor | 0.060MPa,0.15m/sec7 | JISK7218 | 300 | 10^-8mm³/N·m |
| Tensile modulus | | ISO527-2 | 1700 | Mpa |
| Tensile stress | | ISO527-2 | 38.0 | Mpa |
| Nominal tensile fracture strain | | ISO527-2 | 100 | % |
| Bending modulus | | ISO178 | 1500 | Mpa |
| Bending stress | | ISO178 | 51.0 | Mpa |
| friction coefficient | Dynamic2 | JISK7218 | 0.45 | |
| friction coefficient | Steel - Dynamic3 | JISK7218 | 0.50 | |
| Wear factor | 0.49MPa,0.30m/sec4 | JISK7218 | <1.0 | 10^-8mm³/N·m |
| Wear factor | 0.49MPa,0.30m/sec5 | JISK7218 | 50 | 10^-8mm³/N·m |
| Wear factor | 0.060MPa,0.15m/sec6 | JISK7218 | 100 | 10^-8mm³/N·m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 72.0 | °C |
| Linear coefficient of thermal expansion | MD：23to55°C | 内部方法 | 1.3E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1.3E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+14 | ohms |
| Volume resistivity | | IEC60093 | 3E+13 | ohms·cm |
| Dielectric strength | 3.00mm | IEC60243-1 | 18 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 15 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 40 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ColourNumber | | | CF2001 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.