POM DURACON® GM-20 JAPAN POLYPLASTIC

119

Unit Price:
$2991 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
97MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Low warpage Filler: Glass fiber reinf 20% filler by weight
Application Areas:Electronic and electrical Fitness equipment
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:2.00mm	ISO294-4	0.90	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO294-4	1.9	%
Water absorption rate	23°C,24hr	ISO62	0.70	%
Melt volume flow rate	190°C/2.16kg	ISO1133	16.0	cm3/10min
Melt mass flow rate	190°C/2.16kg	ISO1133	21	g/10min
Density/specific gravity		ISO1183	1.54	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress		ISO178	94.0	Mpa
friction coefficient	Dynamic2	JISK7218	0.32
friction coefficient	friction coefficient	Steel - Dynamic3	JISK7218	0.51
Wear factor	0.49MPa,0.30m/sec4	JISK7218	200	10^-8mm³/N·m
	Wear factor	0.060MPa,0.15m/sec5	JISK7218	300	10^-8mm³/N·m
		Wear factor	0.49MPa,0.30m/sec6	JISK7218	7000	10^-8mm³/N·m
		Wear factor	Wear factor	0.060MPa,0.15m/sec7	JISK7218	8000	10^-8mm³/N·m
Tensile stress		ISO527-2	55.0	Mpa
Tensile strain	Break	ISO527-2	5.5	%
Tensile modulus		ISO527-2	3800	Mpa
Bending modulus		ISO178	3500	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	112	°C
Linear coefficient of thermal expansion	MD：23to55°C	内部方法	9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	内部方法	9E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	7E+16	ohms
Volume resistivity		IEC60093	2E+14	ohms·cm
Dielectric strength	3.00mm	IEC60243-1	21	KV/mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO179/1eA	3.6	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ISO2039-2	85

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating		UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ColourNumber			CF3500

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.