POM Iupital™ FU2025 MITSUBISHI ENGINEERING JAPAN
181
- Unit Price:
- $5604 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant High mobility
- Application Areas:Electronic and Electrical Automotive sector
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.35 | ||
| Molding shrinkage rate | ASTM D955 | 1.7 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | ASTM D1238 | 6.0 | g/10min | |
| Shrinkage rate | Flow | 1.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ASTM D785 | 75 | M | |
| Tensile modulus | ASTM D638/ISO 527 | 1600 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 1400 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 48 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 23℃ | ASTM D638 | 34.3 | Mpa |
| Stretching length | 23℃ | ASTM D638 | ＞300 | % |
| bending strength | 23℃ | ASTM D790 | 44.1 | Mpa |
| Bending modulus | 23℃ | ASTM D790 | 1.38 | GPa |
| IZOD impact strength | 3.2mm | ASTM D256 | 180 | J/m |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | >100 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 1.2E-04 | mm/mm.℃ | |
| Hot deformation temperature | -，455Kpa | ASTM D648 | 147 | °C |
| -，820Kpa | ASTM D648 | 94 | °C | |
| Flame retardancy | UL94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257 | 1×10 | ||
| Volume resistivity | ASTM D257 | 1×10 |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dry conditions | 热风干燥 80℃---约3-4小时 | |||
| Processing temperature | 170 | °C | ||
| 190 | °C | |||
| 180 | °C | |||
| 180-210 | °C | |||
| Screw speed | 80-120 | rpm | ||
| Mold temperature | ≦40 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.