Material Description

Technical Data Sheet

Material Description

Material Properties:High rigidity wear resistant Thermal stability High impact resistance
Application Areas:Automotive Applications fibre
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Density/specific gravity		ISO1183	1.38	g/cm³
Melt mass flow rate		ISO1133	12	g/10min
Melt volume flow rate	190°C/2.16kg	ISO1133	10.0	cm3/10min
Shrinkage rate	TD	ISO294-4	1.6	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.7	%
Water absorption rate	Saturation,23°C,2.00mm	ISO62	0.82	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.21	%
MediumDensity			1.18	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	2300	Mpa
Tensile stress	Yield	ISO527-2	56.0	Mpa
Tensile strain	Yield	ISO527-2	18	%
Nominal tensile fracture strain		ISO527-2	35	%
TensileCreepModule	1hr	ISO899-1	2300	Mpa
Tensile creep modulus	1000hr	ISO899-1	1200	Mpa
Bending modulus		ISO178	2100	Mpa
Bending stress	3.5%Strain	ISO178	60.0	Mpa
CoefficientFriction	vs.Itself-Dynamic,1hr	ASTMD1894	0.22

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	146	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	78.0	°C
Vicat softening temperature	--	ISO306/A50	172	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B50	140	°C
Melting temperature 2		ISO11357-3	178	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	1.3E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	1.2E-04	cm/cm/°C
AnnealingTemperature			160	°C
AnnealingTime-Optional			30.0	min/mm

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	1E+15	ohms
Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Relative permittivity	100Hz	IEC60250	3.60
Relative permittivity	Relative permittivity	1MHz	IEC60250	3.60
Leakage Trace Index		IEC60112	600	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179/1eA	9.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	14	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	330	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak
Impact strength of cantilever beam gap	-40°C	ISO180/1A	9.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	14	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale	ISO2039-2	79
Rockwell hardness	Rockwell hardness	R-Sale	ISO2039-2	117

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate 3	1.00mm	ISO3795	45	mm/min
UL flame retardant rating	0.75mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.75mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO6452	2E-04	g

Supplementary Information	Test Method	Test Result	Unit
Emission	VDA275	<8.00	mg/kg
EmissionofOrganicCompounds	VDA277	3.40	µgC/g
SpecificWear-Against	ASTMD1894	40.0	10^-6mm³/N·m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.