POM Delrin® 900P DUPONT THAILAND

119

Unit Price:
$5481 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:wear resistant High rigidity high strength enhance High impact resistance High mobility
Application Areas:Thin walled products Fiber grade
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Density/specific gravity		ISO1183	1.42	g/cm³
Melt mass flow rate		ISO1133	25	g/10min
Melt volume flow rate	190°C/2.16kg	ISO1133	21.0	cm3/10min
Shrinkage rate	TD	ISO294-4	1.9	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.9	%
Water absorption rate	Saturation,23°C,2.00mm	ISO62	1.4	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.40	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	3300	Mpa
Tensile stress	Yield	ISO527-2	71.0	Mpa
Tensile strain	Yield	ISO527-2	12	%
Nominal tensile fracture strain		ISO527-2	23	%
TensileCreepModule	1hr	ISO899-1	2800	Mpa
Tensile creep modulus	1000hr	ISO899-1	1500	Mpa
Bending modulus		ISO178	3000	Mpa
CoefficientFriction	vs.Itself-Dynamic,1hr	ASTMD1894	0.25

Thermal performance	Test Condition	Test Method	Test Result	Unit
AnnealingTemperature			160	°C
AnnealingTime-Optional			30.0	min/mm
EffectiveThermalDiffusivity			8E-08	m²/s
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	162	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	94.0	°C
Vicat softening temperature		ISO306/B50	160	°C
Melting temperature 2		ISO11357-3	178	°C
Linear coefficient of thermal expansion	MD：23to55°C	ASTME831	1E-04	cm/cm/°C
	Linear coefficient of thermal expansion	MD	ISO11359-2	1.2E-04	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	1.2E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	>1.0E+15	ohms
Volume resistivity		IEC60093	1E+14	ohms·cm
Relative permittivity	100Hz	IEC60250	3.80
Relative permittivity	Relative permittivity	1MHz	IEC60250	3.80
Leakage Trace Index		IEC60112	600	V
Hot-wireIgnition	0.750mm	UL746	8.0	sec

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	8.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	200	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	200	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO180/1A	8.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	7.0	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale	ISO2039-2	92
Rockwell hardness	Rockwell hardness	R-Sale	ISO2039-2	120

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate 3	1.00mm	ISO3795	20	mm/min
UL flame retardant rating	0.8mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.8mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
Extreme Oxygen Index		ISO4589-2	23	%
FMVSS flammability		FMVSS302	B
atomization	F-value(refraction)	ISO6452	95	%
atomization	atomization	G-value(condensate)	ISO6452	2E-04	g

Supplementary Information	Test Condition	Test Method	Test Result	Unit
Emission		VDA275	<8.00	mg/kg
EmissionofOrganicCompounds		VDA277	4.30	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.