LLDPE DOWLEX™ 2047G DOW SPAIN
130
- Unit Price:
- $1487 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Thin film grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 2.3 | g/10min |
| Density/specific gravity | ASTMD792 | 0.917 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Falling hammer impact | 20.3um | ASTM D-1709B | 210 | g |
| Tensile yield strength (TD) | 20.3um | ASTM D-882 | 8.16 | Mpa |
| Tensile yield strength (MD) | 20.3um | ASTM D-882 | 8.79 | Mpa |
| Tensile elongation at break (MD) | 20.3um | ASTM D-882 | 460 | % |
| Tensile elongation at break (TD) | 20.3um | ASTM D-882 | 650 | % |
| Elmendorf Tear Strength (TD) | 20.3um | ASTM D-1922 | 510 | g |
| Elmendorf Tear Strength (MD) | 20.3um | ASTM D-1922 | 340 | g |
| Tensile fracture strength (TD) | 20.3um | ASTM D-882 | 28.8 | Mpa |
| Tensile strength at break (MD) | 20.3um | ASTM D-882 | 20.1 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTM D-1525 | 97.8 | °C | |
| Vicat softening temperature | ASTMD1525 | 97.8 | °C | |
| Melting temperature | Internal Method | 122 | °C | |
| Melting temperature (DSC) | 内部方法 | 122 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Membrane strength | MD:20µm | ASTMD882 | 176 | J/cm³ |
| TD:20µm | ASTMD882 | 171 | J/cm³ | |
| elongation | MD:Break,20μm | ASTMD882 | 460 | % |
| TD:Break,20μm | ASTMD882 | 650 | % | |
| Elmondov tear strength | MD:20µm | ASTMD1922 | 340 | g |
| TD:20µm | ASTMD1922 | 510 | g | |
| Tensile strength | MD:Yield,20μm | ASTMD882 | 8.79 | Mpa |
| TD:Yield,20μm | ASTMD882 | 8.16 | Mpa | |
| MD:Break,20μm | ASTMD882 | 50.1 | Mpa | |
| TD:Break,20μm | ASTMD882 | 28.8 | Mpa | |
| Falling hammer impact | 20µm | ASTMD1709A | 210 | g |
| Membrane puncture resistance | 20µm | 内部方法 | 22.1 | J/cm³ |
| Film thickness - tested | 20 | µm |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film Piercing Resistance Movement | 20.3um | Internal Method | 22.1 | J/cm³ |
| Film Resilience (MD) | 20.3um | ASTM D-882 | 176 | J/cm4 |
| Film Resilience (TD) | 20.3um | ASTM D-882 | 171 | J/cm³ |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 20.3µm | ASTMD1003 | 0.40 | % |
| 20.3um | ASTM D-1003 | 0.4 | % | |
| gloss | 45°，20.3um | ASTM D-2457 | 95 | |
| 45°,20.3µm | ASTMD2457 | 95 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 190℃/2.16kg | ASTM D-1238 | 2.3 | g/10min |
| Density/specific gravity | ASTM D-792 | 0.917 | g/m3 | |
| film thickness | 20.3 | um |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.