HDPE SABIC® B5429 SABIC SAUDI
221
- Unit Price:
- $1417 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 101MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 0.30 | g/10min |
| 190°C/21.6kg | ISO1133 | 29 | g/10min | |
| 190°C/5.0kg | ISO1133 | 1.5 | g/10min | |
| Resistance to environmental stress cracking | 10%IgepalCO-630,Compression Molded,F50 | ASTMD1693B | 40.0 | hr |
| Density/specific gravity | ISO1183 | 0.954 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 2.00mm,Compression Molded | ISO527-2/1BA/50 | 1050 | Mpa |
| Bending modulus | 2.00mm,Compression Molded | ISO178 | 1250 | Mpa |
| Tensile stress | Yield,2.00mm,Compression Molded | ISO527-2/1BA/50 | 26.0 | Mpa |
| Break,2.00mm,Compression Molded | ISO527-2/1BA/50 | 28.0 | Mpa | |
| Tensile strain | Break,2.00mm,Compression Molded | ISO527-2/1BA/50 | >1000 | % |
| Bending stress | 2.00mm,Compression Molded | ISO178 | 27.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | DIN53765 | 132 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 81.0 | °C |
| Vicat softening temperature | ASTMD15252 | 127 | °C | |
| EnthalpyChange | DIN53765 | 205 | J/g |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C,Compression Molded | ISO180/A | 5.0 | kJ/m² |
| 23°C,Compression Molded | ISO180/A | 12 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D,Compression Molded | ISO868 | 61 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BlowMoldingMeltTemperature | 165到215 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.