| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate (equilibrium, 23 ° C, 50% RH) | | ISO 62 | 2.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO 527-1/1A/1 | 2500 | Mpa |
| Tensile stress (yield) | | ISO 527-2/1A/50 | 65 | Mpa |
| Tensile strain (yield) | | ISO 527-2/1A/50 | 5 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed | ISO 75-2/Bf | 170 | °C |
| Thermal deformation temperature under load | 1.8 MPa, Unannealed | ISO 75-2/Af | 60 | °C |
| Vicat softening temperature | -- | ISO 306/B50 | 215 | °C |
| Vicat softening temperature | -- | ISO 306/A50 | 230 | °C |
| Ball Pressure Test | (60°C) | IEC 60695-10-2 | 通过 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC 60093 | > 1.0E+15 | ohms |
| Volume resistivity | | IEC 62631-3-1 | > 1.0E+13 | ohms·m |
| Leakage Trace Index | | IEC 60112 | 600 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 80 | |
| drying time | | | 3.0 到 4.0 | |
| Suggested maximum moisture content | | | 0.040 到 0.10 | |
| Processing (melt) temperature | | | 270 到 290 | |
| Mold temperature | | | 60 到 100 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | | 无断裂 | |
| Impact strength of simply supported beam without notch | 23°C | | 无断裂 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness (H 358/30) | | ISO 2039-1 | 110 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning rate | 2.00 mm | ISO 3795 | 30 | mm/min |
| Burning rate | 2.00 mm | FMVSS 302 | 30 | mm/min |
| Flammability level | 0.75 mm | | HB | |
| Flammability level | 1.5 mm | | HB | |
| Flammability level | 3.0 mm | | HB | |
| Burning wire flammability index | 1.5 mm | | 600 | °C |
| Burning wire flammability index | 3.0 mm | | 600 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.