PA66 LNP™ STAT-KON™ RX10004-NA1G002 SABIC INNOVATIVE US
97
- Unit Price:
- $4209 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance Thermal stability Filler: Glass fiber reinf 40% filler by weight
- Application Areas:Textile application Home appliance components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：24hr | ASTMD955 | 0.20to0.40 | % |
| TD：24hr | ASTMD955 | 1.0to3.0 | % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.66 | % |
| Equilibrium,23°C,50%RH | ISO62 | 1.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2/5 | 232 | Mpa |
| Break | ISO527-2/5 | 232 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 2.9 | % |
| Break | ISO527-2/5 | 2.9 | % | |
| Tensile modulus | ISO527-2/1 | 14100 | Mpa | |
| Bending stress | ISO178 | 229 | Mpa | |
| Elongation rate 3 | Yield | ASTMD638 | 2.8 | % |
| Tensile modulus 2 | ASTMD638 | 13900 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 210 | Mpa |
| Yield | ASTMD638 | 230 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 12400 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 338 | Mpa |
| Elongation rate 4 | Break | ASTMD638 | 2.9 | % |
| Bending modulus 5 | ISO178 | 11200 | Mpa | |
| Bending strength 5 | Break,50.0mmSpan | ASTMD790 | 337 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 7 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 259 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 244 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 260 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 253 | °C | |
| Linear coefficient of thermal expansion | MD：-30to30°C | ASTMD696 | 3.2E-05 | cm/cm/°C |
| TD：-30to30°C | ASTMD696 | 6.2E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi axis Instrumented Impact Energy | ISO6603-2 | 4.00 | J | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 18.0 | J |
| Unscented Izod Impact Strength 5 | 23°C | ISO180/1U | 86 | kJ/m² |
| Suspended wall beam notch impact strength 6 | 23°C | ISO180/1A | 16 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.