PA66 Zytel® PC310 NC010 DUPONT USA

102

Unit Price:
$6679 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
48.3MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Non enhanced lubrication
Application Areas:Electronic and Electrical furniture Medical field
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	ISO 294-4	1.4	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	1.4	%
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	8.5	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.6	%
Stickiness number		ISO 307	150	cm³/g

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO 527-2	3100	Mpa
Tensile stress	Yield	ISO 527-2	82.0	Mpa
Tensile strain	Yield	ISO 527-2	4.5	%
Nominal tensile fracture strain		ISO 527-2	25	%
Tensile creep modulus	1 hr	ISO 899-1	--	Mpa
Tensile creep modulus	Tensile creep modulus	1000 hr	ISO 899-1	--	Mpa
Bending modulus		ISO 178	2800	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	200	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	70.0	°C
Glass transition temperature 2		ISO 11357-2	60.0	°C
Vicat softening temperature		ISO 306/B50	240	°C
Melting temperature 2		ISO 11357-3	262	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.0E-4	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.1E-4	cm/cm/°C
Effective Thermal Diffusivity			5.00E-8	m²/s

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 62631-3-2	--	ohms
Volume resistivity		IEC 62631-3-1	1.0E+12	ohms·m
Dielectric strength		IEC 60243-1	32	KV/mm
Relative permittivity	1 MHz	IEC 62631-2-1	3.50
Relative permittivity	Relative permittivity	100 Hz	IEC 62631-2-1	3.80
Dissipation factor	100 Hz	IEC 62631-2-1	8.0E-3
Dissipation factor	Dissipation factor	1 MHz	IEC 62631-2-1	0.018
Leakage Trace Index		IEC 60112	600	V

film	Test Condition	Test Method	Test Result	Unit
Elongation - MD	Yield	ISO 527-3	4.5	%

Filling analysis	Test Result	Unit
Melt density	0.970	g/cm³
Top out temperature	190	°C
Specific Heat Capacity of Melt	2790	J/kg/°C
Thermal Conductivity of Melt	0.16	W/m/K

injection	Test Condition	Test Method	Test Result	Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 到 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			280 到 300	°C
Melt Temperature, Optimum			290	°C
Mold temperature			50 到 90	°C
Mold Temperature, Optimum			70	°C
Maintain pressure			50.0 到 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			4.00	s/mm
Maximum Screw Tangential Speed			24	m/min

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	400 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M -Sale	ISO 2039-2	79
Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	121

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5 mm	UL 94, IEC 60695-11-10, -20	V-2
UL flame retardant rating	UL flame retardant rating	0.70 mm	IEC 60695-11-10, -20	V-2
Extreme Oxygen Index		ISO 4589-2	28	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.