PA66 Ultramid® 8233GHS BK102 BASF GERMANY
125
Unit Price:$3141 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 74MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability High impact resistance
- Application Areas:Electrical applications Industrial machinery
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.30 | % | |
| Water absorption rate | 24hr | ASTMD570 | 1.1 | % |
| 23°C,24hr | ISO62 | 1.1 | % | |
| Saturation | ASTMD570 | 6.4 | % | |
| Saturation,23°C | ISO62 | 6.4 | % | |
| Equilibrium,50%RH | ASTMD570 | 1.8 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 1.8 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -40°C | ISO527-2 | 10300 | Mpa |
| bending strength | 23°C | ASTMD790 | 280 | Mpa |
| Bending stress | 23°C | ISO178 | 245 | Mpa |
| Tensile modulus | 23°C | ISO527-2 | 10200 | Mpa |
| 80°C | ISO527-2 | 4820 | Mpa | |
| 120°C | ISO527-2 | 4010 | Mpa | |
| 150°C | ISO527-2 | 3560 | Mpa | |
| Tensile strength | Break,-40°C | ASTMD638 | 230 | Mpa |
| Break,23°C | ASTMD638 | 180 | Mpa | |
| Break,80°C | ASTMD638 | 90.0 | Mpa | |
| Break,121°C | ASTMD638 | 70.0 | Mpa | |
| Tensile stress | Break,-40°C | ISO527-2 | 230 | Mpa |
| Break,23°C | ISO527-2 | 170 | Mpa | |
| Break,80°C | ISO527-2 | 90.0 | Mpa | |
| Break,120°C | ISO527-2 | 70.0 | Mpa | |
| Break,150°C | ISO527-2 | 60.0 | Mpa | |
| elongation | Break,-40°C | ASTMD638 | 3.0 | % |
| Break,23°C | ASTMD638 | 3.5 | % | |
| Break,80°C | ASTMD638 | 7.0 | % | |
| Break,121°C | ASTMD638 | 7.0 | % | |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| Bending modulus | 23°C | ASTMD790 | 8990 | Mpa |
| 23°C | ISO178 | 8500 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 208 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| Peak melting temperature | ASTMD3418 | 220 | °C | |
| Melting temperature (DSC) | ISO3146 | 220 | °C | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 3.8E-05 | cm/cm/°C |
| RTIElec | 0.71mm | UL746 | 130 | °C |
| 1.5mm | UL746 | 140 | °C | |
| 3.0mm | UL746 | 140 | °C | |
| Evolution Calendar intelligent importer | 0.71mm | UL746 | 115 | °C |
| 1.5mm | UL746 | 115 | °C | |
| 3.0mm | UL746 | 120 | °C | |
| RTIStr | 0.71mm | UL746 | 130 | °C |
| 1.5mm | UL746 | 140 | °C | |
| 3.0mm | UL746 | 140 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 218 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 215 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 65 | kJ/m² |
| Falling impact resistance | 23°C | 内部方法 | 4.07 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 121 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.60mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.