PA66 Zytel® 73G30HSL NC010 DUPONT SHENZHEN
136
Unit Price:$4163 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Automotive Applications Electronic and electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 6.3 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 1.9 | % | |
| Shrinkage rate | TD | ISO294-4 | 0.60 | % |
| MD | ISO294-4 | 0.20 | % | |
| MediumDensity | 1.20 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 2280 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 | W/m/K | ||
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Density/specific gravity | ISO1183 | 1.36 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 16 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 15 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 80 | kJ/m² |
| 23°C | ISO179/1eU | 100 | kJ/m² | |
| Ball pressure hardness | H961/30 | ISO2039-1 | 230 | Mpa |
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 3.50 | J |
| Unscented Izod impact strength | 23°C | ISO180/1U | 80 | kJ/m² |
| Tensile creep modulus | 1000hr | ISO899-1 | -- | Mpa |
| Bending modulus | ISO178 | 8500 | Mpa | |
| Bending stress | ISO178 | 280 | Mpa | |
| TensileCreepModule | 1hr | ISO899-1 | -- | Mpa |
| Tensile stress | Break | ISO527-2 | 190 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.5 | % |
| Tensile modulus | ISO527-2 | 9500 | Mpa | |
| Rockwell hardness | R-Scale | ISO2039-2 | 121 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 210 | °C | |
| Vicat softening temperature | ISO306/B50 | 215 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| EffectiveThermalDiffusivity | 9.1E-08 | m²/s | ||
| Melting temperature | ISO11357-3 | 221 | °C | |
| Glass transition temperature | ISO11357-2 | 60.0 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate | 1.00mm | ISO3795 | 50 | mm/min |
| Extreme Oxygen Index | ISO4589-2 | 21 | % | |
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| G-value(condensate) | ISO6452 | 1E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 8.50 | µgC/g | |
| Odor | VDA270 | 3.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.