Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate - flow	23°C, 3.20 mm, Injection	ASTM D955	0.40 到 0.90	%
Water absorption rate	24 hr	ASTM D570	0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Break, 23°C, 3.20 mm, Injection	ASTM D638	191	Mpa
elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	3.0	%
Bending modulus	23°C, 3.20 mm, Injection	ASTM D790	9320	Mpa
bending strength	23°C, 3.20 mm, Injection	ASTM D790	279	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	260	°C
Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	250	°C
Peak melting temperature		ASTM D3418	260	°C
Linear coefficient of thermal expansion - flow		ASTM D696	3.0E-5	cm/cm/°C
RTI Elec	0.75 mm	UL 746	120	°C
	RTI Elec	1.5 mm	UL 746	110	°C
	RTI Elec	RTI Elec	3.0 mm	UL 746	120	°C
RTI Imp	0.75 mm	UL 746	120	°C
	RTI Imp	1.5 mm	UL 746	110	°C
	RTI Imp	RTI Imp	3.0 mm	UL 746	120	°C
RTI	0.75 mm	UL 746	120	°C
	RTI	1.5 mm	UL 746	110	°C
	RTI	RTI	3.0 mm	UL 746	120	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity	23°C	ASTM D257	1.0E+16	ohms·cm
Dielectric strength	23°C, 1.00 mm	ASTM D149	25	KV/mm
Dielectric constant	23°C, 1 MHz	ASTM D150	4.00

injection	Test Result	Unit
drying temperature	80 到 100	°C
drying time	4.0 到 5.0	hr
Temperature at the rear of the barrel	260 到 270	°C
Temperature in the middle of the barrel	270 到 285	°C
Temperature at the front of the material cylinder	270 到 290	°C
Spray nozzle temperature	270 到 295	°C
Processing (melt) temperature	270 到 295	°C
Mold temperature	80 到 110	°C
Back pressure	29.4 到 58.8	Mpa
Screw speed	30 到 60	rpm

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale, 23°C, Injection	ASTM D785	122

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75 mm	UL 94	HB
	UL flame retardant rating	1.5 mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.