PA66 66IK4 NC DOMO CHEM GERMANY

130

Unit Price:
$5294 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Toughened grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow : 23°C, 72hr	ISO 2577	1.6 到 1.8	%
Shrinkage rate	Shrinkage rate	流量 : 23°C, 72hr	ISO 2577	1.4 到 1.6	%
Stickiness number	96% H2SO4	ISO 307	145	cm³/g

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Yield	ISO 527-2/50	45.0	Mpa
Tensile strain	Break	ISO 527-2/50	> 50	%
Tensile modulus		ISO 527-2/1	1800	Mpa
Bending modulus 3		ISO 178	1700	Mpa
Bending stress 3		ISO 178	65.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Melting temperature		ISO 11357-3	262	°C
Vicat softening temperature		ISO 306/B50	220	°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	160	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	65.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	1.0E+13	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm

injection	Test Result	Unit
drying temperature	75 到 85	°C
Processing (melt) temperature	270 到 290	°C
Mold temperature	40 到 80	°C
drying time	2.0 到 4.0	hr

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Unscented Izod impact strength	23°C	ISO 180/1U	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R -Sale	ISO 2039-2	110

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate		FMVSS 302	< 100	mm/min
UL flame retardant rating	0.8 mm	UL 94	HB
ISO 9660		ISO 1874	PA66-I,M,14-020

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.