| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 1.2 | % |
| Shrinkage rate | MD | ISO294-4 | 0.20 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 4.3to4.7 | % |
| HumidityAbsorption-62%RH | 70°C | ISO1110 | 1.7to1.9 | % |
| SpiralFlow2.3 | | 内部方法 | 72.0 | CM |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2/1 | 13100 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 225 | Mpa |
| Tensile strain | Break | ISO527-2/5 | 3.0 | % |
| Bending modulus 4 | | ISO178 | 12000 | Mpa |
| Bending stress 4 | | ISO178 | 360 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| TemperatureIndex | 50%LossofTensileStrength,5000hr | IEC216 | 160to175 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 260 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 260 | °C |
| Hot deformation temperature | 8.0MPa,Unannealed | ISO75-2/C | 225 | °C |
| Melting temperature 5 | | DINEN11357-1 | 262 | °C |
| TemperatureIndex | 50%LossofTensileStrength,20000hr | IEC216 | 130to150 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+12 | ohms |
| Volume resistivity | | IEC60093 | 1E+13 | ohms·cm |
| Leakage Trace Index | SolutionA | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 95 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 100 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | H961/30 | ISO2039-1 | 270 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning rate 6 | 1.00mm | FMVSS302 | <100 | mm/min |
| FlameRating | 1.6mm | UL94 | HB | |
| GlowWireFlammability Index | 1.6mm | IEC60695-2-12 | 650 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ReinforcementContent | | ISO1172 | 40 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.