PA66 LUMID® GN1001BF KA30 LG CHEM KOREA
102
- Unit Price:
- $3119 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Halogen-free
- Application Areas:Connector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate - flow | 23°C, 3.20 mm, Injection | ASTM D955 | 0.90 到 1.6 | % |
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 1.3 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield, 23°C, 3.20 mm, Injection | ASTM D638 | 78.5 | Mpa |
| elongation | Break, 23°C, 3.20 mm, Injection | ASTM D638 | 28 | % |
| Bending modulus | 23°C, 6.40 mm, Injection | ASTM D790 | 3330 | Mpa |
| bending strength | 23°C, 6.40 mm, Injection | ASTM D790 | 113 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 6.40 mm, Injection | ASTM D648 | 230 | °C |
| 1.8 MPa, Unannealed, 6.40 mm, Injection | ASTM D648 | 85.0 | °C | |
| Peak melting temperature | ASTM D3418 | 260 | °C | |
| Linear coefficient of thermal expansion - flow | ASTM D696 | 7.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 23°C | ASTM D257 | 1.0E+14 | ohms·cm |
| Dielectric strength | 23°C, 1.00 mm | ASTM D149 | 22 | KV/mm |
| Dielectric constant | 23°C, 1 MHz | ASTM D150 | 3.00 | |
| Leakage Trace Index | IEC 60112 | 600 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 到 100 | °C | ||
| drying time | 4.0 到 5.0 | hr | ||
| Suggested maximum moisture content | 0.10 | % | ||
| Temperature at the rear of the barrel | 255 到 270 | °C | ||
| Temperature in the middle of the barrel | 260 到 275 | °C | ||
| Temperature at the front of the material cylinder | 260 到 275 | °C | ||
| Spray nozzle temperature | 270 到 280 | °C | ||
| Processing (melt) temperature | 260 到 280 | °C | ||
| Mold temperature | 60 到 90 | °C | ||
| Back pressure | 0.490 到 1.96 | Mpa | ||
| Screw speed | 60 到 200 | rpm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale, 23°C, Injection | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40 to 0.82 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.