Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow : 23°C, 2.00 mm | ISO 294-4 | 2.1 | % |
| 流量 : 23°C, 2.00 mm | ISO 294-4 | 2.2 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 8.5 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 2.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2 | 2850 | Mpa |
| Tensile stress | Yield, 23°C | ISO 527-2 | 85.0 | Mpa |
| Break, 23°C | ISO 527-2 | 55.0 | Mpa | |
| Tensile strain | Yield, 23°C | ISO 527-2 | 5.0 | % |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 40 | % |
| Bending modulus | 23°C | ISO 178 | 3000 | Mpa |
| Bending stress | 23°C | ISO 178 | 80.0 | Mpa |
| Poisson's ratio | ISO 527-2 | 0.40 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 200 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 65.0 | °C | |
| Melting temperature | ISO 11357-3 | 260 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 55°C, 2.00 mm | ISO 11359-2 | 1.0E-4 | cm/cm/°C |
| Across Flow : 23 to 55°C, 2.00 mm | ISO 11359-2 | 1.0E-4 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 0.750 mm | IEC 60093 | 1.0E+14 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 60 到 75 | °C | ||
| drying time | 4.0 | hr | ||
| Suggested maximum moisture content | 0.050 到 0.10 | % | ||
| Suggested maximum recycled material ratio | 25 | % | ||
| Temperature at the rear of the barrel | 280 到 310 | °C | ||
| Temperature in the middle of the barrel | 280 到 310 | °C | ||
| Temperature at the front of the material cylinder | 280 到 310 | °C | ||
| Spray nozzle temperature | 280 到 310 | °C | ||
| Processing (melt) temperature | 285 到 305 | °C | ||
| Mold temperature | 65 到 95 | °C |
| squeeze | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Temperature in Zone 1 of the material cylinder | 280 到 295 | °C | ||
| Temperature in Zone 2 of the material cylinder | 280 到 295 | °C | ||
| Temperature in Zone 3 of the material cylinder | 280 到 295 | °C | ||
| Temperature in Zone 4 of the material cylinder | 280 到 295 | °C | ||
| Temperature in Zone 5 of the material cylinder | 280 到 295 | °C | ||
| Melt Temperature | 270 到 295 | °C | ||
| Oral mold temperature | 270 到 295 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.