PA66 AKROMID® A3 GF 60 1 AKRO-PLASTIC GERMANY

210

Unit Price:
$2840 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Thermal stability high strength High rigidity
Application Areas:Engineering accessories Industrial applications Automotive sector
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
SpiralFlow2.3		内部方法	53.0	CM
Shrinkage rate	TD	ISO294-4	0.80	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.40	%
Water absorption rate	Saturation,23°C	ISO62	3.2to3.7	%
HumidityAbsorption-62%RH	70°C	ISO1110	1.0to1.2	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2/1	20500	Mpa
Tensile stress	Break	ISO527-2/5	260	Mpa
Tensile strain	Break	ISO527-2/5	2.0	%
Bending modulus 4		ISO178	19800	Mpa
Bending stress 4		ISO178	400	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	260	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	260	°C
	Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	235	°C
Melting temperature 5		DINEN11357-1	262	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	1E+12	ohms
Volume resistivity		IEC60093	1E+13	ohms·cm
Leakage Trace Index	SolutionA	IEC60112	600	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	97	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	100	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness	H961/30	ISO2039-1	330	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate 6	1.00mm	FMVSS302	<100	mm/min
UL flame retardant rating	0.8mm	UL94	HB
GlowWireFlammability Index	1.6mm	IEC60695-2-12	650	°C

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ReinforcementContent		ISO1172	60	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.