PA66 Zytel® HTNFR51G35L BK337 DUPONT SHENZHEN

120

Unit Price:
$4494 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Aging resistance High temperature resistan Glass fiber reinforced enhance Flame retardant
Application Areas:Electrical appliances Household appliances Automotive interior equip
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	Saturation,23°C,2.00mm	ISO62	4.5	%
Shrinkage rate	TD	ISO294-4	0.60	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.20	%
SpecificHeatCapacity of Melt			1860	J/kg/°C
ThermalConductivityofMelt			0.25	W/m/K

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	12000	Mpa
Tensile stress	Break	ISO527-2	210	Mpa
Tensile strain	Break	ISO527-2	2.4	%
TensileCreepModule	1hr	ISO899-1	--	Mpa
Tensile creep modulus	1000hr	ISO899-1	--	Mpa
Bending modulus		ISO178	10300	Mpa
Bending stress		ISO178	300	Mpa
Poisson's ratio		ISO527	0.39

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	284	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	260	°C
Melting temperature 2		ISO11357-3	300	°C
Linear coefficient of thermal expansion	MD：--	ISO11359-2	1.8E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO11359-2	1.8E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO11359-2	5.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to23°C	ISO11359-2	5.5E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	--	ohms
Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Dielectric strength		IEC60243-1	36	KV/mm
Relative permittivity	100Hz	IEC60250	4.00
Relative permittivity	Relative permittivity	1MHz	IEC60250	4.00
Leakage Trace Index		IEC60112	600	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	70	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale	ISO2039-2	108
Rockwell hardness	Rockwell hardness	R-Sale	ISO2039-2	124

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate 3	1.00mm	ISO3795	23	mm/min
UL flame retardant rating	0.9mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.9mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
Extreme Oxygen Index		ISO4589-2	24	%
FMVSS flammability		FMVSS302	B

Supplementary Information	Test Condition	Test Method	Test Result	Unit
Odor		VDA270	4.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.