PA66 SCHULAMID® RBL 2500 A SCHULMAN USA
217
Unit Price:$5323 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 25% filler by weight
- Application Areas:--
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 23℃ | % | 0.10到0.31 | |
| 饱和,23℃ | % | 3.5到5.0 | ||
| 平衡,23℃,50%RH | % | 1.2到1.5 |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸应力 | 断裂,23℃ | MPa | 144.83到292.41 | |
| 拉伸应变 | 断裂,23℃ | % | 1.9到3.1 | |
| 拉伸模量 | 23℃ | MPa | 8206.9到28000.0 |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔融温度 | °C | 260 | ||
| 连续使用温度 | °C | 110到220 | ||
| 8.0Mpa,未退火 | °C | 65到220 | ||
| 横向 | mm/mm/°C | 68.6E-5到127.0E-5 | ||
| 流动 | mm/mm/°C | 142.2E-5到203.2E-5 | ||
| 1.8MPa,未退火 | °C | 230到250 |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 介电强度 | 23℃ | V/mil | 840 | |
| 体积电阻率 | 23℃ | ohms·cm | 1.0E+12到1.0E+14 |
| 冲击性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 简支梁无缺口冲击强度 | 23℃ | kJ/m² | 11.143到19.964 |
| 硬度 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 球压硬度 | MPa | 222.76到370.34 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.