PA66 Zytel® 70G43HSL BK DUPONT USA

Unit Price:
$3890 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
99.2MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility Low crud
Application Areas:Electronic and electrical Automotive components
Color:--
Grade:Impact resistant grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	ISO 294-4	0.90	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	0.30	%
Water absorption rate	24 hr, 23°C, 2.00 mm	ISO 62	0.90	%
	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	4.7	%
	Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.5	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Break	ISO 527-2	225	Mpa
Tensile strain	Break	ISO 527-2	2.5	%
Tensile modulus		ISO 527-2	14000	Mpa
Bending modulus 2		ISO 178	12500	Mpa
Bending stress 2		ISO 178	340	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Glass transition temperature 3		ISO 11357-2	80.0	°C
Melting temperature 3		ISO 11357-3	262	°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	258	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	255	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC 62631-3-1	> 1.0E+13	ohms·m
Dissipation factor	100 Hz	IEC 62631-2-1	0.013
Dissipation factor	Dissipation factor	1 MHz	IEC 62631-2-1	0.015
Dielectric strength		IEC 60243-1	25	KV/mm
Leakage Trace Index		IEC 60112	600	V

Filling analysis	Test Condition	Test Method	Test Result	Unit
Top out temperature			210	°C
Thermal Conductivity of Melt			0.25	W/m/K

injection	Test Condition	Test Method	Test Result	Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 到 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			285 到 300	°C
Melt Temperature, Optimum			295	°C
Mold temperature			70 到 120	°C
Mold Temperature, Optimum			100	°C
Maintain pressure			50.0 到 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min

Impact performance	Test Condition	Test Method	Test Result	Unit
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	4.40	J
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate	1.00 mm	ISO 3795	27	mm/min
FMVSS flammability		FMVSS 302	B
Extreme Oxygen Index		ISO 4589-2	24	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.