PA66 LATAMID 66 H2 G/60 LATI ITALY
109
- Unit Price:
- $4168 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 21.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 60% filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:2.00mm | ISO294-4 | 0.60to0.85 | % |
| MD:2.00mm | ISO294-4 | 0.30to0.50 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.26 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- | ISO527-2/1 | -- | Mpa |
| 23°C | ISO527-2/1 | 22500 | Mpa | |
| 60°C | ISO527-2/1 | 18000 | Mpa | |
| 90°C | ISO527-2/1 | 11000 | Mpa | |
| Tensile strain | Break,60°C | ISO527-2/5 | 2.6 | % |
| Break,90°C | ISO527-2/5 | 5.7 | % | |
| Break,120°C | ISO527-2/5 | 7.0 | % | |
| Break,150°C | ISO527-2/5 | 7.5 | % | |
| Tensile modulus | 120°C | ISO527-2/1 | 6600 | Mpa |
| 150°C | ISO527-2/1 | 5800 | Mpa | |
| Tensile stress | Break | ISO527-2/5 | -- | Mpa |
| Break,23°C | ISO527-2/5 | 235 | Mpa | |
| Break,60°C | ISO527-2/5 | 180 | Mpa | |
| Break,90°C | ISO527-2/5 | 130 | Mpa | |
| Break,120°C | ISO527-2/5 | 100 | Mpa | |
| Break,150°C | ISO527-2/5 | 75.0 | Mpa | |
| Tensile strain | Break | ISO527-2/5 | -- | % |
| Break,23°C | ISO527-2/5 | 2.2 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 255 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 235 | °C | |
| Continuous use temperature 3 | 135 | °C | ||
| Vicat softening temperature | ISO306/B50 | 240 | °C | |
| Linear coefficient of thermal expansion | MD：30to100°C | ISO11359-2 | 6E-06 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 55 | kJ/m² |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dimensional Stability | 63.0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.