PA66 Zytel® ST801HS BK010 DUPONT JAPAN
292
- Unit Price:US$ 5,490 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High impact resistance
- Application Areas:Fitness equipment｜Bottle cap｜Automotive sector
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.07 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 1.4 % | |
| ISO 294-4 | 1.8 % | ||
| Water absorption rate | ISO 62 | 1.1 % | |
| ISO 62 | 6.5 % | ||
| ISO 62 | 2.0 % | ||
| viscosity number | ISO 307 | 130 cm³/g |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | ISO 3795 | < 100 mm/min | |
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB | ||
| Limiting Oxygen Index | ISO 4589-2 | 20 % | |
| FMVSS combustion rate | FMVSS 302 | B |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2000 Mpa | |
| tensile strength | ISO 527-2 | 49.0 Mpa | |
| Tensile strain | ISO 527-2 | > 50 % | |
| Tensile creep modulus | ISO 899-1 | -- Mpa | |
| ISO 899-1 | -- Mpa | ||
| Flexural modulus | ISO 178 | 1800 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 20 kJ/m² | |
| ISO 179/1eA | 70 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | -- | |
| Impact strength of cantilever beam gap | ISO 180/1A | 20 kJ/m² | |
| ISO 180/1A | 15 kJ/m² | ||
| ISO 180/1A | 80 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ejection Temperature | 190 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 62631-3-2 | -- ohms | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m | |
| dielectric strength | IEC 60243-1 | 25 KV/mm | |
| relative permittivity | IEC 62631-2-1 | 3.30 | |
| IEC 62631-2-1 | 3.50 | ||
| Dissipation Factor | IEC 62631-2-1 | 5.0E-3 | |
| IEC 62631-2-1 | 0.010 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Melt Temperature, Optimum | 290 °C | ||
| Temperature | 50 to 100 °C | ||
| Mold Temperature, Optimum | 80 °C | ||
| pressure holding | 50.0 to 100 Mpa | ||
| yes | |||
| Hold Pressure Time | 4.00 s/mm | ||
| Maximum Screw Tangential Speed | 18 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 157 °C | |
| ISO 75-2/A | 63.0 °C | ||
| Glass Transition Temperature | ISO 11357-2 | 75.0 °C | |
| vicat | ISO 306/B50 | 205 °C | |
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | ASTM E831 | 1.4E-4 cm/cm/°C | |
| ISO 11359-2 | 1.4E-4 cm/cm/°C | ||
| ISO 11359-2 | 1.1E-4 cm/cm/°C | ||
| ISO 11359-2 | 1.6E-4 cm/cm/°C | ||
| ASTM E831 | 1.3E-4 cm/cm/°C | ||
| ISO 11359-2 | 1.3E-4 cm/cm/°C | ||
| ISO 11359-2 | 1.1E-4 cm/cm/°C | ||
| ISO 11359-2 | 1.3E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.