PA66 Leona™ CR301 X01 ASAHI JAPAN
105
- Unit Price:
- $6466 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:dimensional stability Conductive
- Application Areas:Electrical field Electrical components Electronic field Industrial applications Switch panel
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.48 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.5 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | -- | % | |
| Equilibrium, 23°C, 50% RH | ISO 62 | -- | % | |
| Shrinkage rate - flow rate | 内部方法 | 0.50 到 1.3 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break, 23°C | ISO 527-2 | 85.0 | Mpa |
| -- | ASTM D638 | 88.0 | Mpa | |
| Taber abraser | 1000 Cycles | ASTM D1044 | -- | mg |
| elongation at break | ASTM D638/ISO 527 | 3 | % | |
| Tensile modulus | 23°C | ISO 527-2 | 7000 | Mpa |
| tensile strength | ASTM D638/ISO 527 | 88 | kg/cm²(MPa)[Lb/in²] | |
| elongation | Break | ASTM D638 | 3.0 | % |
| Break, 23°C | ISO 527-2 | 2.0 | % | |
| Rockwell hardness | ASTM D785 | 85 | ||
| Bending modulus | -- | ASTM D790 | 5900 | Mpa |
| 23°C | ISO 178 | 7400 | Mpa | |
| bending strength | -- | ASTM D790 | 147 | Mpa |
| 23°C | ISO 178 | 140 | Mpa | |
| ASTM D790/ISO 178 | 147 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed | ASTM D648 | 250 | °C |
| 0.45 MPa, Unannealed | ISO 75-2/B | 249 | °C | |
| 1.8 MPa, Unannealed | ASTM D648 | 191 | °C | |
| 1.8 MPa, Unannealed | ISO 75-2/A | 188 | °C | |
| Linear coefficient of thermal expansion - flow | ASTM D696 | 4.0E-5 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 51 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTM D785 | 85 | |
| M -Sale | ISO 2039-2 | 85 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.