PA66 Zytel® ST801AW NC010 DUPONT USA
142
Unit Price:$5572 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance
- Application Areas:Fitness equipment Bottle cap Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 1.4 | % |
| 流量 | ISO 294-4 | 1.8 | % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 1.1 | % |
| Saturation, 23°C, 2.00 mm | ISO 62 | 6.5 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 | % | |
| Stickiness number | ISO 307 | 130 | cm³/g | |
| density | ISO 1183 | 1.07 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | -- | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 20 | kJ/m² |
| 23°C, Partial Break | ISO 179/1eA | 70 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 20 | kJ/m² |
| -30°C | ISO 180/1A | 15 | kJ/m² | |
| 23°C | ISO 180/1A | 80 | kJ/m² | |
| Tensile stress | 50% Strain | ISO 527-2 | 49.0 | Mpa |
| Tensile strain | Break | ISO 527-2 | > 50 | % |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- | Mpa |
| 1000 hr | ISO 899-1 | -- | Mpa | |
| Tensile modulus | ISO 527-2 | 2000 | Mpa | |
| Bending modulus | ISO 178 | 1800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 157 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 63.0 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 55°C | ASTM E831 | 1.4E-4 | cm/cm/°C |
| Flow | ISO 11359-2 | 1.4E-4 | cm/cm/°C | |
| Flow : -40 to 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Flow : 55 to 160°C | ISO 11359-2 | 1.6E-4 | cm/cm/°C | |
| Across Flow : 23 to 55°C | ASTM E831 | 1.3E-4 | cm/cm/°C | |
| Across Flow | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| Across Flow : -40 to 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Across Flow : 55 to 160°C | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| Vicat softening temperature | ISO 306/B50 | 205 | °C | |
| Glass transition temperature | ISO 11357-2 | 75.0 | °C | |
| Melting temperature | ISO 11357-3 | 262 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC 60243-1 | 25 | KV/mm | |
| Relative permittivity | 1 MHz | IEC 62631-2-1 | 3.30 | |
| 100 Hz | IEC 62631-2-1 | 3.50 | ||
| Leakage Trace Index | IEC 60112 | 600 | V | |
| Surface resistivity | IEC 62631-3-2 | -- | ohms | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 | ohms·m | |
| Dissipation factor | 100 Hz | IEC 62631-2-1 | 5.0E-3 | |
| 1 MHz | IEC 62631-2-1 | 0.010 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Top out temperature | 190 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Drying time - hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Processing (melt) temperature | 280 到 300 | °C | ||
| Melt Temperature, Optimum | 290 | °C | ||
| Mold temperature | 50 到 100 | °C | ||
| Mold Temperature, Optimum | 80 | °C | ||
| Maintain pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 4.00 | s/mm | ||
| Maximum Screw Tangential Speed | 18 | m/min |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ISO 4589-2 | 20 | % | |
| Burning rate | 1.00 mm | ISO 3795 | < 100 | mm/min |
| UL flame retardant rating | 0.8 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| FMVSS flammability | FMVSS 302 | B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.